Urethane Casting Resin- 75 Shore D
For orders placed before 2:30PM EST
WARNING: This product can expose you to chemicals including Diisodecyyl Phthalate, which is known to the State of California to cause Birth Defects or Other Reproductive Harm. For more information go to www.P65Warnings.ca.gov
Get Superior Stiffness for Detailed Castings
For final parts and short-run castings, this white Urethane Casting Resin with 75 Shore D hardness can create detailed parts with superior cosmetic qualities. #3475 Urethane Casting Resin has a simple 1:1 mix ratio, and its low mixed viscosity makes it an ideal material to fill complicated molds. Cured castings are bright white and have great physical properties including: good tensile strength and superior stiffness in thin sections.
#3475 Urethane Casting Resin is a great material for high performance parts and castings. It can be used for the casting of prototypes to simulate molded parts or for the preproduction checking of injection molds. Common application include automobile, aircraft and marine parts and tooling. As a low viscosity material, it can be hand injected into the most detailed cavities.
When mixed thoroughly, pour the urethane slowly to aid the release of air bubbles. When using Urethane Casting Resin – 75 Shore D kits, avoid water and all types of moisture contamination. Do not use any urethane kit with PVA Release Film, and do not mix with wooden mixing sticks or in paper mixing containers. #2333 Plastic Paint Stirrers for Urethanes are recommended. To ensure a proper release from a mold, use at least four layers of #4121 Non-Silicone High Temp Paste Wax.
#3475 Urethane Casting Resin can fully cure at room temperature. Demold time for heavier section castings is 4 to 6 hours @ 77°F. Castings will develop strength sufficient for most applications in 18 to 24 hours at 77°F, and reach full cure in 7 days at room temperature. The full cure can be accelerated by oven curing after the material gels at room temperature. Oven cure at 150°F for 2-3 hours or oven cure at 120°F for 4-6 hours. Heat curing will increase the heat distortion temperature, and therefore improve the heat stability of the cured material.
- Mix Ratio (by weight) – 100:100
- Color – White
- Working Time, 4 fl. Oz. mass @ 77°F – 30-40 minutes