System 4500 Infusion Epoxy Resin
For orders placed before 2:30PM EST
WARNING: This product can expose you to chemicals including Bisphenol A (BPA), which is known to the State of California to cause birth defects or other reproductive harm. For more information go to www.P65Warnings.ca.gov.
Low Viscosity Infusion Epoxy
Our System 4500 is a low viscosity epoxy system designed for the fabrication of parts and structures by the resin infusion method. This system flows extremely well, and produces dense, void-free laminates. The superior cured properties of this system produce items with good strength and toughness with excellent long-term stability. Combine this resin system with any of our Carbon Fiber, Kevlar or most fiberglass fabrics for lightweight, superior-strength composite parts.
This Infusion Epoxy System is available with two hardener options, a 40 minute pot life and a 70 minute pot life. The two hardener options are identical except for reaction time, so no matter which hardener is chosen, you can expect the same high performance properties. The mixed viscosity with both hardeners allows the material to flow very well, even in thin walled areas. It penetrates heavy fabric sections and wets out quickly for further ease of production.
Both hardeners will cure completely at room temperature, if required. The material will gel hard overnight at ambient temperatures around 77°(F). At this point in the cure, the bag and infusion materials can be removed from the laminate and the part can be sanded or trimmed as required. Full cure with these two hardeners will be achieved in 4 to 6 days at normal room temperature. A heat cure will shorten the curing time of System 4500 Infusion Epoxy. In situations where the laminate can be placed in an oven after a room temperature gel, curing times of 8 to 10 hours at 180°F or 14 to 18 hours at 150°F will provide 90% of full cured properties.
- Will cure completely at room temperature, if necessary.
- Mixed viscosity around 300 centipoise, so resin flows easily.
- This epoxy system does not contain methylene dianiline (MDA), or any other potentially harmful aniline derivatives.
- Two hardener options to fit your project needs.
- Allow material to gel completely prior to removal from mold.
- Add heat to decrease post-gel cure times to as little as 8-10 hours.
|Mix Ratio||4:1 (Resin:Hardener)|
|Pot Life||4570 - 70 Min|
|4540 - 40 Min|